| Items | Units | Data | Test | Remark | |
| Inherent Viscosity | dL/g | 0.76±0.015 | GB/T14190- 2017-5.1.1 | The greater viscosity is the higher | |
| mechanical properties | |||||
| Carboxy | mol/ton | ≤35 | GB/T14190- 2017-5.4.2 | The higher conten will reduces the thermal stability of the product | |
| Color | B | / | ≤2.2 | GB/T14190- 2017-5.5.2 | The higher value is the yellower color |
| L | / | ≥56 | Transparencia | ||
| Di-ethylene glycol | % | ≤1.4 | GB/T14190- 2017-5.2.1 | Reduce light and heat resistance of materials | |
| Moisture content | % | ≤0.2 | GB/T14190- 2017-5.7.2 | The process causes degradation of polyester | |
| Ash content | % | ≤0.05 | GB/T14190- 2017-5.10 | The impurity content,which are derived from metal oxides decomposed by catalysts, raw materials and mechanical impurities produced during the production process | |
| Density | g/cm³ | 1.28 | GB/T1033.1 -2008 | ||
1 .The Viscosity is phenol and tetrachloroethane mixed solvent 1:1,and test temp is 25℃ .
2.The widely applied to the surface layer of film and sheet, with good printing performance, suitable for various ink and glue. It can solve the problems of losing point and low inking in shallow screen printing.